laves

英 [leɪvz]

美 [leɪvz]

v.  洗涤；沐浴；冲刷（缓慢）流过（经）
lave的第三人称单数

双语例句

• The effects of rapid quenching on the initial activation capabilities of AB_2 Laves phase electrode alloys were investigated comprehensively. The phase structures and morphologies of as-cast and quenched alloys were determined and observed by XRD and SEM.
  研究了快淬处理对AB2型Laves相电极合金初始活化性能的影响，用XRD和SEM分析了铸态及快淬态合金的相结构，并观察了合金的微观组织形貌。
• The effects of the Ti/ Zr ratio and Mn/ Cr ratio on the hydrogen storage properties of Ti Mn based laves phase hydrogen storage alloys were investigated.
  研究了不同的Ti/Zr比以及Mn/Cr比对Ti-Mn基Laves相贮氢合金贮氢性能的影响；
• The Development of Zr-Based Laves Phase Hydrogen Storage Eleetrode Materials
  锆系Laves相贮氢电极材料的研究进展
• Defect structure in NbCr_2 Laves-phase intermetallics and its toughening effect
  Laves相NbCr2金属间化合物的缺陷结构及其韧化效应
• Effect of Mechanical Alloying on Oxidation Behavior at 1100 ℃ of Laves Phase NbCr_2 Alloys by Hot Pressing Synthesis
  机械合金化对热压合成Laves相NbCr2合金1100℃氧化行为的影响
• Besides, the effects of both valence charge and atomic radius on Laves phase structures are in opposition to each other in transition-lanthanide ( actinides) alloys.
  对过渡-镧系（锕系）元素组成的合金，B原子的价电子数对其Laves相结构影响最为明显，且价电子和原子半径对Laves相结构的影响作用互为反向。
• Electronic Structure and Mechanical Properties of Mg-Al-Ca Laves Phase and Mg-Al-Sb Alloys
  Mg-Al-CaLaves相和Mg-Al-Sb合金的电子结构和力学性能
• The results show that a lot of intermetallic compounds(μ phase and Laves phase) and carbides ( MC, M 23 C 6 and M 6C) precipitated at same time from the alloy after solution treating and aging.
  结果表明，经过固溶和时效处理后合金中同时析出大量金属间化合物和碳化物。金属间化合物主要为μ相和Laves相，碳化物主要为MC、M23C6和M6C。
• The results show that anti-site defects exist in the ZrCr_2 Laves phase.
  结果表明：当ZrCr2Laves相成分偏离化学计量比时，ZrCr2中存在着反位置（组分）缺陷。
• HREM observation on long-period stacking structure of zr ( cr, v)_2 Laves phase
  Zr（Cr，V）2Laves相长周期堆垛结构的高分辨电子显微术观察